Ferroelectric Al1−xScxN has raised much interest in recent years due to its unique ferroelectric properties and complementary metal oxide semiconductor back-end-of-line compatible processing temperatures. Potential applications in embedded nonvolatile memory, however, require ferroelectric materials to switch at relatively low voltages. One approach to achieving a lower switching voltage is to significantly reduce the Al1−xScxN thickness. In this work, ferroelectric behavior in 5–27 nm films of sputter deposited Al0.72Sc0.28N has been studied. We find that the 10 kHz normalized coercive field increases from 4.4 to 7.3 MV/cm when reducing the film thickness from 27.1 to 5.4 nm, while over the same thickness range, the characteristic breakdown field of a 12.5 μm radius capacitor increases from 8.3 to 12.1 MV/cm. The 5.4 nm film demonstrates ferroelectric switching at 5.5 V when excited with a 500 ns pulse and a switching speed of 60 ns. 

Due to their favorable electromechanical properties, such as high sound velocity, low dielectric permittivity and high electromechanical coupling, Aluminum Nitride (AlN) and Aluminum Scandium Nitride (Al1−xScxN) thin films have achieved widespread application in radio frequency (RF) acoustic devices. The resistance to etching at high scandium alloying, however, has inhibited the realization of devices able to exploit the highest electromechanical coupling coefficients. In this work, we investigated the vertical and lateral etch rates of sputtered AlN and Al1−xScxN with Sc concentration x ranging from 0 to 0.42 in aqueous potassium hydroxide (KOH). Etch rates and the sidewall angles were reported at different temperatures and KOH concentrations. We found that the trends of the etch rate were unanimous: while the vertical etch rate decreases with increasing Sc alloying, the lateral etch rate exhibits a V-shaped transition with a minimum etch rate at x = 0.125. By performing an etch on an 800 nm thick Al0.875Sc0.125N film with 10 wt% KOH at 65 °C for 20 min, a vertical sidewall was formed by exploiting the ratio of the 1011¯ planes and 11¯00 planes etch rates. This method does not require preliminary processing and is potentially beneficial for the fabrication of lamb wave resonators (LWRs) or other microelectromechanical systems (MEMS) structures, laser mirrors and Ultraviolet Light-Emitting Diodes (UV-LEDs). It was demonstrated that the sidewall angle tracks the trajectory that follows the 1¯212¯ of the hexagonal crystal structure when different c/a ratios were considered for elevated Sc alloying levels, which may be used as a convenient tool for structure/composition analysis.